Artifical Stone Mold Making Liquid Silicone Rubber

• Material: Organic Silicone
• Application: Industrial
• Certification: ISO, RoHS, SGS, MSDS
• Min Order: 200kg
• Form: Liquid Rubber
• Color: Clear
• Model NO.: 902-40, 902-30, H8225, H8230
• Production Time: One Week
• Certificate: CE RoHS
• Port: Tianjin Port
• Service: Offer Technology Service
• Transport Package: Plastic Pail or Metal Pail on Pallets
• Specification: 10KG, 20KG, 40KG, 50KG
• Trademark: XD silicone
• Origin: Beijing
• HS Code: 3910000000
• Production Capacity: 200 Ton /Month

Product Description

Appilications: 
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects

Features: 
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding

Technical data sheet:

Model	902-40	902-30	H8225	H8230
Mixing ratio (A:B)	100:2~3	100:2~3	1:1	1:1
Hardness (Shore A)≥	25	30	25	30
Tear-strength (kgf/c m²)≥	21	22	25	26
Viscosity ( mixed 25°C mpa.S)	25000±2000	25000±2000	18000±2000	20000±2000
Shrinkagerate (%)≤	0.2	0.2	0.1	0.1
Elongation(%)	450	400	450	400

How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.

2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.

3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.

4.At  25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.

Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.